MAR-MR-EasePA12-CF Carbon Fiber Reinforced 3D Printing Consumables Surface Quality and High Strength
Specification:
| Model No | MR-EasePA12-CF | Cable Net Weight | 1kg |
| Color | Black | Nozzle Temperature | 280-300℃ |
| Bed Temp | 40-70℃ | Print Speed |
30-120mm/s |
| Bed | PEI film or coating with PVP glue | Fan | Off |
| Cable Size | 1.75mm | Feature | High flowability hardness |
Product Description:
MAR-MR-EasePA12-CF is specially developed for FDM 3D printing process, and its substrate material is PA12 long-chain nylon, which has low density, low moisture absorption, high strength, high abrasion resistance, excellent chemical resistance and high heat resistance. It also has good dimensional stability, no warpage and no shrinkage during the printing process, and can be used with Green Quick-Remove support material to solve the problem of poor molding effect on the support surface of complex models.
Material Properties:
|
Property |
Testing method |
Typical value |
|
Density |
ISO 1183 |
1.06 g/cm³ |
|
Water absorption |
ISO 62: Method 1 |
0.6 % |
|
Melting Temperature |
ISO 11357 |
167℃ |
|
Melt index |
260℃, 2.16kg |
11 |
|
Determination of temperature |
ISO 75: Method A |
105℃ (1.80MPa) |
|
ISO 75: Method B |
125℃ (0.45MPa) |
|
|
Tensile strength(X-Y) |
ISO 527 |
74.48±2.85 MPa |
|
Young’s modulus(X-Y) |
3113.73±349.0 MPa |
|
|
Elongation at break (X-Y) |
3.84±0.20 % |
|
|
Bending strength (X-Y) |
ISO 178 |
116.4±4.17 MPa |
|
Bending modulus (X-Y) |
3603.79±353.81 MPa |
|
|
Charpy impact strength （X-Y） |
ISO 179 |
8.03±0.66 KJ/㎡ |
|
Single shell Z-axis tensile strength |
Custom method: Vase mode/ Nozzle size 0.6mm/Layer height 0.3mm/ Layer time 20s |
31.98 ± 1.96 MPa |
Specimens printed under the following conditions: Nozzle temp 300°C, Bed temp 80℃, Print speed 45mm/s, Infill 100%, Infill angle ±45°
Additional Suggestions:
1. Nylon material is very easy to absorb moisture within the environment, and printing after absorbing moisture will result ozzing, extruding with bubbles and rough surface appearance, thus reducing print quality. It is recommended that put the filament into a dry box (humidity below 15%) immediately after opening the EasePA12-CF vacuum foil bag for printing. Please put the unused filament back into the original aluminum foil bag for sealed storage.
2. After the material is damp, there will be more printing ozzing, bubbles extruded and rough printing surface. Please dry the filament in an oven at 80-100℃ for 4-6h to restore the printing quality of EasePA12-CF.
3. It is recommended to use hardened steel and above grade nozzles made by Phaetus, which can effectively improve the print quality. Besides, it is recommended that the thickness of the heating block is longer 12mm.
4. After the printing is completed, the printed part can be annealed to further improve the strength of print part. Annealing conditions: leave printing part in an oven at 80-100℃ for 4 to 8 hours and cool to room temperature naturally.