MAR High Temperature Nylon 15% Carbon Fiber Teinforced 3D Printing Material UltraPA-CF Industrial Grade Consumables

MAR High Temperature Nylon 15% Carbon Fiber Teinforced 3D Printing Material UltraPA-CF Industrial Grade Consumables

Regular price $89.85 USD
Regular price $105.71 USD Sale price $89.85 USD
Sale Sold out
weight
color

MAR High Temperature Nylon 15% Carbon Fiber Teinforced 3D Printing Material UltraPA-CF Industrial Grade Consumables

 

Specification: 

Model No MR-UltraPA-CF Cable Net Weight 1kg
Color Black Nozzle Temperature 300-320℃
Bed Temp 70-80℃ Print Speed

30-60mm/s

Bed PEI film or coating with PVP glue   Fan Off
Cable Size 1.75mm Feature 15%Carbon Fiber Reinforced PAHT

Product Description:

MAR MR-UltraPA-CF is specially developed for FDM 3D printing process, and its substrate material is high temperature nylon, which has low moisture absorption, high strength, high abrasion resistance, excellent chemical resistance and high heat resistance. It also has good dimensional stability, no warpage and no shrinkage during the printing process

High Temperature Nylon 15% Carbon Fiber


Material Properties:

Property

Testing method

Typical value

Density

ISO 1183

1.15 g/cm³

Water absorption

ISO 62: Method 1

0.6 %

Melting Temperature

ISO 11357

231℃

Melt index

260℃, 2.16kg

10.78

Determination of temperature

ISO 75: Method A

113℃ (1.80MPa)

ISO 75: Method B

188℃ (0.45MPa)

Tensile strength(X-Y)

ISO 527

121.77±4.28 MPa

Young’s modulus(X-Y)

7807.99±517.99MPa

Elongation at break (X-Y)

1.88±0.11 %

Bending strength (X-Y)

ISO 178

190.85±2.07 MPa

Bending modulus (X-Y)

8512.22±241.31 MPa

Charpy impact strength (X-Y)

ISO 179

7.74±1.13 KJ/㎡

Single shell Z-axis tensile strength

Custom method: Vase mode/

Nozzle size 0.6mm/Layer height 0.3mm/

Layer time 20s

 41.9 ± 3.87 MPa

Specimens printed under the following conditions: Nozzle temp 320°C, Bed temp 80℃, Print speed 45mm/s, Infill 100%, Infill angle ±45°

Additional Suggestions:

 

1. Nylon material is very easy to absorb moisture within the environment, and printing after absorbing moisture will result ozzing, extruding with bubbles and rough surface appearance, thus reducing print quality. It is recommended that put the filament into a dry box (humidity below 15%) immediately after opening the UltraPA-CF vacuum foil bag for printing. Please put the unused filament back into the original aluminum foil bag for sealed storage. 

2. After the material is damp, there will be more printing ozzing, bubbles extruded and rough printing surface. Please dry the filament in an oven at 80-100℃ for 4-6h to restore the printing quality of UltraPA-CF. 

3. It is recommended to use hardened steel and above grade nozzles made by Phaetus, which can effectively improve the print quality. Besides, it is recommended that the thickness of the heating block is longer 12mm. 

4. After the printing is completed, the printed part can be annealed to further improve the strength of print part. Annealing conditions: leave printing part in an oven at 80-100℃ for 4 to 8 hours and cool to room temperature naturally.