Skip to product information
1 of 5

Mayrc

Mayrc MR-Tough-PETG Pink 3D printing material 10kg High Flow Toughness Modification PETG for Can Handle

Mayrc MR-Tough-PETG Pink 3D printing material 10kg High Flow Toughness Modification PETG for Can Handle

Regular price $20.90 USD
Regular price $24.59 USD Sale price $20.90 USD
Sale Sold out
weight
color

Mayrc MR-Tough-PETG Pink 3D printing material 10kg High Flow Toughness Modification PETG for Can Handle

Specification: 

Model No

MR-Tough-PETG

Cable Net Weight

1kg/roll

Color

Pink 

Nozzle Temperature

220-250℃

Bed Temp

70-80℃

Print Speed

30-90mm/s

Bed

Glass,PC or PEI   

Cooling fan speed

On

Cable Size

1.75mm

Feature

High flow

Recommended support material

MAR™ MR-PVA

Recommended Nozzle Diameter

0.2-1.0mm

Raft separation distance

0.2-0.25mm

Retraction distance

2-5mm

Retraction speed

1800-3600 mm/min

 

Notice:The bonding between MR-Tough-PET and the PC bottom plate is very strong. When printing a larger bottom surface, the distance between the first layer of the model and the bottom plate can be appropriately adjusted.

Product Description:

MR-Tough-PETG is a tough PETG specially developed for FDM3D printing technology, and at the same time it has advanced printing performance by improving the fluidity of the material. Compared with PLA, it has better mechanical strength and heat resistance


pink 1kg 10kg printing material

Product Advantages:

1.High Impact Resistance

The notched impact strength of MR-Tough-PETG is increased to more than twice that of ordinary PETG without affecting the interlayer bonding strength in the Z-axis direction

2.Easy to Print

MR-Tough-PETG has excellent material fluidity and good molding effect, which can be printed first in most printers.


Material Properties:

Property

Testing method

Typical value

Density

ISO 1183

1.24 g/cm³

Melting Temperature

ISO 11357

78℃

Melt index

220℃, 2.16kg

13.2g/10min

Determination of temperature

ISO 75: Method A

73℃ (1.80MPa)

ISO 75: Method B

78℃ (0.45MPa)

Tensile strength(X-Y)

ISO 527

40.3±0.6 MPa

Young’s modulus(X-Y)

1780±80MPa

Elongation at break (X-Y)

10.1±0.6 %

Bending strength (X-Y)

ISO 178

62.8±0.4 MPa

Bending modulus (X-Y)

1919±54 MPa

Charpy impact strength (X-Y)

ISO 179

13.9±23KJ/㎡

Specimens printed under the following conditions: Nozzle temp 300°C, Bed temp 80℃, Print speed 45mm/s, Infill 100%, Infill angle ±45°

Toughness modification PETG

Disclaimer:

The typical values presented in this data sheet are intended for reference and comparison purposes only. They should not be used for design specifications or quality control purposes. Actual values may vary significantly with printing conditions. End- use performance of printed parts depends not only on materials, but also on part design, environmental conditions, printing conditions, etc. Product specifications are subject to change without notice.

Each user is responsible for determining the safety, lawfulness, technical suitability, and disposal/recycling practices of Mar materials for the intended application. Mar makes no warranty of any kind, unless announced separately, to the fitness for any use or application. Mar shall not be made liable for any damage, injury or loss induced from the use of Mar materials in any application.


 



View full details